Product Feature of Electronic Potting Silicone Rubber
HY-9055 silicone rubber is a kind of low viscosity, Inherent flame resistance, two components addtion cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time. It can be applied to electronic components for insulation, waterproofing, fixed and flame retardant. It mainly applied in electronic components surface with materials of PC(Poly-carbonate)PP ABS PVC, etc. and metal materials.
2. Typical Application of Electronic Potting Silicone Rubber
HY-9055 electronic potting silicone rubber could be applied to
- high powered electronics,
- DC/DC module and circuit board which requires heat dissipation and high temperature resistance.
-It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc.
3. Technical Guidelines of of Electronic Potting Silicone Rubber
a, Pls put part A and part B in separate container and stir evenly before mixing the two part together.
b, Mixing Ratio: part A: part B = 1:1
c, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes.Then the mixture could be used for pouring.
Note: The thickness of the silicone affects the curing time. If the silicone used is a little thick,then the curing time will be a little longer.The temperature also affects the curing time.When in lower temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. With temperature of 80?100?, the silicone will cure in 15 minutes; while in 25? room temperature, the silicone will cure around 8 hours.
electronic potting silicon Rubber Characteristics
1. No toxicity, solventless, no odor or cure by-product.
2.No significant exotherm or shrinkage during curing.
3.Flexible curing schedule, can be cured at room temperature (R.T.) or at elevated temperature.
4.Very stable to changes of temperature, stability over wide temperature range (-50 to 200 C).
5.Good thermal conductivity.
6.Excellent dielectric properties for maintaining and protection of existing electrical insulation requirements.
7.Excellent weather resistance and waterproof property for protection from moisture and dust contamination.
8.Relative easier removal benefits to repair of electrical/electronic devices
9.Green environmental protection.
Applicationof electronic potting silicon Rubber
- high powered electronics
- LED, LCD electronic display
- circuit board
- PCB substrate,etc
- Precision Electronic Components,
- DC/DC module and circuit board protection which requires high transparency and recovery.
electronic potting silicon Rubber Warm Tips
1. The electronic potting silicon rubber should be sealed storage.The mixture should be used up at
once, avoid causing waste.
2. The electronic potting silicon rubber belongs to non-dangerous goods, but keep away from
mouth and eyes.
3. When electronic potting silicon rubber gets stratified after a period of storage, Please mix the
electronic potting silicon rubber evenly before using, it does not affect the performance
Electronic Potting Silicone Rubber is a kind of low viscosity, Inherent flame resistance, two components addition cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time. It can be applied to electronic components for insulation, waterproofing, fixed and flame retardant. It mainly applied in electronic components surface with materials of PC(Poly-carbonate)ã??PPã??ABSã??PVC, etc. and metal materials.
2. Typical Application of Electronic Potting Silicone Rubber
HY-9055 electronic potting silicone rubber could be applied to
- high powered electronics,
- DC/DC module and circuit board which requires heat dissipation and high temperature resistance.
-It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc.
1. Product Feature of Electronic Potting Silicone Rubber
Electronic Potting Silicone Rubber is a kind of low viscosity, Inherent flame resistance, two components addition cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time. It can be applied to electronic components for insulation, waterproofing, fixed and flame retardant. It mainly applied in electronic components surface with materials of PC(Poly-carbonate)PPABSPVC, etc. and metal materials.
2. Typical Application of Electronic Potting Silicone Rubber
HY-9055 electronic potting silicone rubber could be applied to
- high powered electronics,
- DC/DC module and circuit board which requires heat dissipation and high temperature resistance.
-It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc.
3. Technical Guidelines of of Electronic Potting Silicone Rubber
a, Pls put part A and part B in separate container and stir evenly before mixing the two part together.
b, Mixing Ratio: part A: part B = 1:1
c, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes.Then the mixture could be used for pouring.
Note: The thickness of the silicone affects the curing time. If the silicone used is a little thick,then the curing time will be a little longer.The temperature also affects the curing time.When in lower temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. With temperature of 80ï½?100, the silicone will cure in 15 minutes; while in 25 room temperature, the silicone will cure around 8 hours.
4.Notes of Electronic Potting Silicone Rubber
a.The following material may hinder the curing of HY-9055, So pls use after the test. When necessary, pls clean the application areas.
Organotin compound or Condensation silicone with organotin
Sulphur, sulfide and sulfur rubber materials.
Amine compounds as well as contains the amine materials.
Pewters solder flux
b. HY-9055 should be sealed storage.The mixture should be used up disposably to avoid causing waste.
c. HY-9055 belongs to non-dangerous goods, but keep away from mouth and eyes.
d. When it gets stratified after a period of storage, Please mix it evenly before using,which does not affect the performance
Description
HY-9045 is a kind of low viscosity, Inherent flame resistance, two components addtion cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time.
Application
HY-9045 is suitable for bonded seal of electronic components, power module and control module, LED invertor potting, etc which requires waterproof and insulation. It can be broadly used for LED screen, Wind Power Generator, PCB, substrate, etc.
1. Product feature of electronic potting silicone rubber
eat dissipation and high temperature resistance.
-it can be broadly used for led screen, wind power generator, pcb substrate, etc.
3. Technical guidelines of of electronic potting silicone rubber
A, pls put part a and part b in separate container and stir evenly before mixing the two part together.
B, mixing ratio: part a: part b = 1:1
C, deaeration the mixture in vacuum pump under 0.08 mpa for 3-5 minutes.Then the mixture could be used for pouring.
Note: the thickness of the silicone affects the curing time. If the silicone used is a little thick, then the curing time will be a little longer.The temperature also affects the curing time.When in lower temperature, we suggest customers appropriately temperature, the silicone will cure around 8 hours.
Description
HY-210 can be applied to the sealing and pouring of various electronic components, and then forming insulation system with no corrosion and negligible shrinkage.
Application
HY-210 is suitable for bonded seal of electronic components, power module and control module, LED invertor potting, etc which requires waterproof and insulation. It can be broadly used for LED screen, Wind Power Generator, PCB, substrate, etc.
Technical Parameters
Model Color Viscosity (cps) Hardness (A°) Mixing ratio Operating
Time(min) Curing
Time(hr, 25â??)
HY-210 Translucent/ Light yellow/ Red brown 1800±800 15±3 10:1 30~60 4~5
Characteristics
Room temperature vulcanize, and easy to operate;
Maintain flexibility at a wide temperature range, and excellent insulation performance;
Waterproof, moisture-proof, mouldproof, dustproof, and stable components;
Resistance to Chemical dielectric, anti-yellowing, resistance to climate ageing.
Operation instructions
1, Pls put part A and part B in separate container and stir evenly before mixing the two part together.
2, Weight Ratio: part A: part B = 1:1
3, Deaeration the mixture under 0.08 MPa for 3 minutes.
4, The temperature influences the curing time of 9301. When in too low temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization.
Warm tips :
1.The following material may hinder the curing of the product, So pls apply after summary experiment. When necessary, pls clean the application areas.
Condensation silicone which not completely cured or organic tin compounds
Sulphur, sulfide and sulfur rubber materials.
Amine compounds as well as contains the amine materials.
Pewters solder flux.
2. Should be sealed storage.The mixture should be used up at once, avoid causing waste.
3. Silicone belongs to non-dangerous goods, but keep away from mouth and eyes.
4. When it gets stratified after a period of storage, Please mix 9301 evenly before using, it does not affect the performance.
Package
20KG/drum vacuum packing for part A + 2KG/drum vacuum packing for part B
Shelf life
Twelve(12) months when stored under dry and cool place by original package under 25â??
Y-9055 silicone rubber is a kind of low viscosity, Inherent flame resistance, two components addition cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time. It can be applied to electronic components for insulation, waterproofing, fixed and flame retardant. It mainly applied in electronic components surface with materials of PC(Poly-carbonate)ã?�PPã?�ABSã?�PVC, etc. and metal materials.
Electronic potting compound silicone
Technical guidelines of electronic potting silicon rubber
1, please put part a and part b in separate container and stir evenly before mixing the two part together.
2, weight ratio: part a: part b = 1:1
3, deaeration the mixture under 0.08 m pa for 3 minutes.
4, the temperature influences the curing time of 9355 electronic potting silicon rubber. When in too low temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization. Warm tips of electronic potting silicon rubber: 1.The following material may hinder the curing of the product.So please apply after summary experiment. When necessary, please clean the application areas.
Condensation silicone which not completely cured or organic tin compounds
Sulfur, sulfide and sulfur rubber materials.
Amine compounds as well as contains the amine materials.
Pewters solder flux. 2. Should be sealed storage.The mixture should be used up at once, avoid causing waste.
3. Electronic potting silicon rubber belongs to non-dangerous goods, but keep away from mouth and eyes.
4. When electronic potting silicon rubber gets stratified after a period of storage, please mix 9301 evenly before using, it does not affect the performance.
1. Product Feature of Addition cure Electronic Potting Silicone Rubber
Electronic Potting Silicone Rubber is a kind of low viscosity, Inherent flame resistance, two components addition cured potting silicone with heat-conducting. It cures with both on room temperature and heated temperature. It has the feature of the higher temperature the faster of the curing time. It can be applied to electronic components for insulation, waterproofing, fixed and flame retardant. It mainly applied in electronic components surface with materials of PC(Poly-carbonate)ã?�PPã?�ABSã?�PVC, etc. and metal materials.
2. Typical Application of Addition cure Electronic Potting Silicone Rubber
HY-9055 electronic potting silicone rubber could be applied to
- high powered electronics,
- DC/DC module and circuit board which requires heat dissipation and high temperature resistance.
-It can be broadly used for LED screen, Wind Power Generator, PCB substrate, etc.
3. Technical Guidelines of of Addition cure Electronic Potting Silicone Rubber
a, Pls put part A and part B in separate container and stir evenly before mixing the two part together.
b, Mixing Ratio: part A: part B = 1:1
c, Deaeration the mixture in vacuum pump under 0.08 MPa for 3-5 minutes.Then the mixture could be used for pouring.
4.Notes of Addition cure Electronic Potting Silicone Rubber
a.The following material may hinder the curing of HY-9055, So pls use after the test. When necessary, pls clean the application areas.
Organotin compound or Condensation silicone with organotin
Sulphur, sulfide and sulfur rubber materials.
Amine compounds as well as contains the amine materials.
Pewters solder flux
b. HY-9055 should be sealed storage.The mixture should be used up disposably to avoid causing waste.
c. HY-9055 belongs to non-dangerous goods, but keep away from mouth and eyes.
d. When it gets stratified after a period of storage, Please mix it evenly before using,which does not affect the performance.
PACKAGE
40Kg/pail as a set (Part A 20Kg + Part B 20Kg)
SHELF LIFE AND TRANSPORTATION
1. Twelve(12) months when stored at 24C in tightly closed original packages.
2. This kind of product is non-dangerous product, which could be transported as general chemicals.
3. Storage beyond the expired date doesnot necessarily mean that the product is no longer usable. In this case however, the properties required for the intended use must be checked for quality assurance reasons.
Black color pcb electronic potting silicone hy-215
Technical parameters for pcb electronic potting silicone
Properties indexPart aPart b
Before curingAppearenceBlack fluidColorless / yellowish fluid
Viscosisty (cps)2500±500-
Features when operationMixing ratio ( by weight)10:1
Operating time (25c /min)20~30
Curing time ( hr, basically cured)3
Curing time ( hr, perfectly cured)24
Hardness(shore a)15+/-3
After curingThermal conductivity[w( m·k)]=0.4
Dielectric strength( kv/mm)=25
Dielectric permittivity(1.2mhz)3.0~3.3
Volume resistivity(o·cm)=1.0×1016
Fire resistance94-v1
(pls note all data of pcb electronic potting silicone rubber with black color above is in 25c with 55% humidity conditions. We don't guarantee a same date if testing under different conditions, or when data was regenerated).
Warm tips for for pcb electronic potting silicone
1. Sealing pakage for storage. The mixture should be used up at once to avoid wasting.
2. Silicone belongs to non-dangerous goods, but keep away form mouth and eyes.
3. When it gets stratified after a period of storage, please mix hy-210# evenly before using,
it does not affect the performance.
Shelf life and transportation
1. Twelve(12) months when stored at 25c in original unopened packages.
2. This is a non-dangerous product, it can be transported as general chemicals.
3. Products exceed the storage life should be confirmed normal before using.
Ferro silicon Specs: Si:75%min. and Si:72%min. C:0.2%max. S:0.02%max. P:0.04%max. Al:2.0%max.1.5%max.and 1.0%max .Commodity: Ferro Silicon Low Al Specs: Si:75%min. C:0.2%max. S:0.02%max. P:0.04%max.Al:0.1%max.0.3%max.and0.5%max. In 1mt plastic woven bags.
Ferro Silicon Ferro Silicon has a melting point of 1200�¯�¿�½?�?�°C to 1250�¯�¿�½?�?�°C with a boiling point of 2355�¯�¿�½?�?�°C and Ferro Silicon contains about 2% of calcium and alluminium. Ferro Silicon, as an additive to the production process of ferrous metals, will impart several desirable properties upon the resultant alloy. Some of the primary benefits of adding Ferro Silicon to an alloy is to improve the corrosion resistant properties of the new compound, as well as to add to the high temperature heat- resistance properties of the new alloy, for example, in the production of silicon steel for use in transformer cores.
FerroChrome is a kind of Ferro alloy which is formed by Ferro and Chrome,it is an important alloy addition in steel making. Ferrochrome (Fe Cr) is an alloy of chromium and containing between 50% and 70% chromium.
Addition cure silicon rubber for artificial stone products pplications:
It mainly use for making molds for resin, stone, gypsum and cement product with medium size.
Addition cure silicon rubber for artificial stone products Typical Datasheet :
Item No Color Hardness (A°) Viscosity (CS) Tensile-strength( kgf /cm2 ) Tear-strength (kgf /cm2) Elongation-break(%) Mixing Ratio of silicone and catalyst Application(most for resin, stone, gypsum and cement product to make moulds)
HY-E635 Translucent 35±2 8000±2000 =60 =13 =400 1:1
Addition cure silicon rubber for artificial stone products Points of attention:
1,Prone to poisoning, can not mix with condensation, ionic compounds containing N, S-, P, organic matter and of Sn, As, Hg, Ph., easy molding plastic poisoning, resulting in the phenomenon of not curing.
2,Comparing with Condensation cure silicone, Addition cure silicone's adhesive properties to be worse.
3,Addition cure silicone affect by temperature greatly when cured under room temperature.
4,Addition cure silicone is easy to poisoning, please clean the tools which are used for condensation silicone rubber, so that it can avoid poisoning.
It’s fobidden to add the pigment or powder to addition cure silicone rubber arbitrarily,it’s easy to make the catalyst to be poisoning.
5,Addition cure silicone rubebr has two-component, the component A and component B, please pay attention to clean the component A containers before using for the component B, and vice versa
6,In order to avoid the hardness change, we should mix the component A and component B according to its mixing ratio strictly, no atter it’s 1 : 1 or 10 : 1.
Silicone rubber surfactant (Organic silicone surface additive) Application:
It can be used as a spray modifier, foliar absorption aids, activation agent, widely used herbicide, liquid nutrients, growth regulators, insecticides, fungicides, which do not decompose the original pesticide, can greatly reduce the surface tension of the solution, reducing the contact between the droplet and the leaf angle, surface enhanced the liquid in the plant or pest surface wetting, adhesion, and a spreader, thereby improving efficacy.
Silicone surfactant ZINCA-2000 is lower phytotoxicity and environmental hazards than the normal fatty amines, ethoxylated alcohol surfactant, and greatly reduce human and environmental impact.
Introduction of liquid rtv silicone for electronic patrs sealing
liquid rtv silicone for electronic patrs sealing is a two-component room temperature cure potting compound with mix ratio of 1: 1, curing time can be accelerated by heating up, features with good flow ability and flame resistance. It's suitable for encapsulating of LED displayers, power module and electronics components, etc.
Features of liquid rtv silicone for electronic patrs sealing
Easy mix with 1: 1 proportion
Low viscosity, good flow ability
Room temperature cure or heat up cure
Thermal conduction, flame resistance
Without solvent
Using Instructions of liquid rtv silicone for electronic patrs sealing
1. Preparing: Clean up the coating surface, remove the rust, dust, oil dirt.
2. Pouring: Weigh the silicone and catalyst correctly, mix silicone part A and part B thoroughly, pour onto the electronic components/surface after vacuum degassing.
3. Curing: Room temperature cure or heat-up cure is both workable.
4. It should be use up after open the package, the material must be kept in a cool place sealed well, and it should avoid from contact with moisture in the air.
Packaging of liquid rtv silicone for electronic patrs sealing
Packs are available in 20kg and 200kg per drum.
Storage & Transportation of electronic potting compound silicone rubber
1. Keep it from strong sunshine, heat, and store in cool & dry place, well sealed. It has a shelf life of 12 months.
2. It can be stroked and transported as non-dangerous goods.
Technical guidelines of liquid rtv silicone for electronic patrs sealing :
1. Pls put part A and part B in separate container and stir evenly before mixing the two part\ together.
2. Weight Ratio: part A: part B = 10:1
3. Deaeration the mixture under 0.08 MPa for 3 minutes.
4. The temperature influences the curing time of electronic potting silicone rubber.
5. When in too low temperature, we suggest customers appropriately heat the mixture to accelerate vulcanization.
Warm tips for liquid rtv silicone for electronic patrs sealing :
1. The electronic potting silicon rubber should be sealed storage.The mixture should be used up at
once, avoid causing waste.
2. The electronic potting silicone rubber belongs to non-dangerous goods, but keep away from
mouth and eyes.
3. When electronic potting silicone rubber gets stratified after a period of storage, Please mix the
electronic potting silicone rubber evenly before using, it does not affect the performance