Black color pcb electronic potting silicone hy-215
Technical parameters for pcb electronic potting silicone
Properties indexPart aPart b
Before curingAppearenceBlack fluidColorless / yellowish fluid
Viscosisty (cps)2500±500-
Features when operationMixing ratio ( by weight)10:1
Operating time (25c /min)20~30
Curing time ( hr, basically cured)3
Curing time ( hr, perfectly cured)24
Hardness(shore a)15+/-3
After curingThermal conductivity[w( m·k)]=0.4
Dielectric strength( kv/mm)=25
Dielectric permittivity(1.2mhz)3.0~3.3
Volume resistivity(o·cm)=1.0×1016
Fire resistance94-v1
(pls note all data of pcb electronic potting silicone rubber with black color above is in 25c with 55% humidity conditions. We don't guarantee a same date if testing under different conditions, or when data was regenerated).
Warm tips for for pcb electronic potting silicone
1. Sealing pakage for storage. The mixture should be used up at once to avoid wasting.
2. Silicone belongs to non-dangerous goods, but keep away form mouth and eyes.
3. When it gets stratified after a period of storage, please mix hy-210# evenly before using,
it does not affect the performance.
Shelf life and transportation
1. Twelve(12) months when stored at 25c in original unopened packages.
2. This is a non-dangerous product, it can be transported as general chemicals.
3. Products exceed the storage life should be confirmed normal before using.