Chlorosulfonated polyethylene anticorrosive paint is formulated with chlorosulfonated polyethylene resin, anti-corrosive and antirust pigments, fillers and additives. It has primer, intermediate paint and finish paint.
The product is chemically inert, has good resistance to the atmosphere, moisture, salt, alkali, acids, oxidants and petroleum, has excellent outdoor weather resistance, and the coating film is tough and has excellent wear resistance. No need to remove the stubborn old coating during maintenance.
Wet-on-wet application with 3 minutes flash off time.
* Single baking at 130 C for 25 min. High productivity & Low production cost.
* Recommended for welded areas as the composite system at 40-60 (Primer + Topcoat) gives minimum Salt Spray life of 240 Hrs.
It is mainly used for anticorrosion of metal workpieces, bridge steel structures, pipeline handrail, etc., featuring large area application, high performance price ratio, thinning after adding water, environmental friendly, no harm.
Synthetic Red Oxide Primer
Ritver Synthetic Red Oxide Primer Commercial is based on Alkyd resin containing anticorrosive pigments. It is used as a primer coat for many applications especially for protecting the metals and other steel structures against corrosion and is quite versatile. It forms a firm base with good adhesion for Ritver Topcoat Enamels and Ritver Quick Drying Enamels.
2869 Anticorrosive Primer Suppliers
Short on time? Let Anticorrosive Primer sellers contact you.
ARP326
PLASTIC PRIMER
A transparent single component primer that promotes adhesion of subsequent coats of paint on most plastic substrates particularly those used in automotive.
Chlorosulfonation Polyethylene Anticorrosive Primer
Chlorosulfonated polyurethane paint is formulated with chlorosulfonated polyethylene resin, anti-corrosive and antirust pigments, fillers and additives. It has primer, intermediate paint and finish paint.
The product is chemically inert, has good resistance to the atmosphere, moisture, salt, alkali, acids, oxidants and petroleum, has excellent outdoor weather resistance, and the coating film is tough and has excellent wear resistance. No need to remove the stubborn old coating during maintenance.
This product is mainly used in petrochemical equipment, pipelines and other facilities that are corroded by the chemical atmosphere. It can also be used in storage tanks and other chemical equipment that are corroded by acid, alkali, and salt, and in facilities that require waterproofing such as reservoirs, water tanks, and sewage pools.
Advantages OF Chlorosulfonation Polyethylene Primer
Excellent corrosion resistance
Good resistance to water, acid, alkali and chemicals.
Good adhesion to all kinds of substrates
Specification of Chlorosulfonation Polyethylene Anticorrosive Primer
Type Solvent
Solid Content 46%
Mixing Ratio two components Part A: Part B=10:1 by weight
Dry Film Thickness 50m per coat
Specific Gravity 1.15kg/Liter
Coverage Rate (Theoretical) 0.14kg/m2/50m 0.122L/m2/50m
Drying Time Temperature 5 10 20 30
Dry to touch 30mins 20mins 15mins
Dry Hard 5hrs 3.5hrs 3hrs
Package 22kgs for one kit, part A 20kgs, part B 2kgs
Where are the chlorosulfonated polyethylene coatings mainly used?
It is mainly used for equipment, facilities, pipelines corroded by the chemical atmosphere, and storage tanks and equipment corroded by acid, alkali, and salt. It can also be used for water-proof facilities such as reservoirs, water tanks, and sewage pools.
As a paints manufacturer, we will do our best to meet all the needs of customers.
MASONARY PRIMER
It is specially formulated to give a very high level of adhesion and deep penetration into the concrete, which also offers a medium level of opacity.