High purity al2o3 alumina ceramic ball as ball mill grinding media
Product information
HS code 69091200.00
Application The product is widely used in precision processing and deep processing of various ceramics, enamels, glasses and hard materials in chemical factories, as grinding media for fine crushing machines like ball mills, can-type mills and vibration mills.
MOQ 1KG
Sample Free samples are available
Application:Industrial ceramic grinding mediaï¼?grinding
Al2O3 content:92%,95%
Making type:Rolling; ISP
HRA: 85
Type:Ceramic Balls,alumina grinding media balls
Appearance:Smooth and white
Color:white
Compressing strength:2000Mpa
Size:0.5mm-95mm
Advantage: High wear resistance
Production temperature:1600
HS code:690912
Certificate:ISO 9000
Application:Industrial ceramic grinding media
Self Abrasion:0.0055-0.01%
Al2O3 content:92%,95%
Making type:Rolling; ISP
HRA: 85
Type:Ceramic Balls,alumina grinding media balls
Appearance:Smooth and white
Color:white
Compressing strength:2000Mpa
Size:0.5mm-95mm
Advantage: High wear resistance
HS code:690912
Certificate:ISO 9000
Application:Industrial ceramic grinding media
Self Abrasion:0.0055-0.01%
Al2O3 content:92%,95%
Making type:Rolling; ISP
HRA: 85
Type:Ceramic Balls,alumina grinding media balls
Appearance:Smooth and white
Color:white
Compressing strength:2000Mpa
Size:0.5mm-95mm
Advantage: High wear resistance
HS code:690912
Certificate:ISO 9000
Application:Industrial ceramic grinding mediagrinding
Self Abrasion:0.0055-0.01%
Density:3.60g/cm33.7g/cm3
Al2O3 content:92%,95%
Making type:Rolling; ISP
Moh's hardness:9
HRA: 85
Water absorption:0.01%
Type:Ceramic Balls,alumina grinding media balls
Appearance:Smooth and white
Color:white
Compressing strength:2000Mpa
Size:0.5mm-95mm
Advantage: High wear resistance
Production temperature:1600
HS code:690912
Fe2O3:0.02%
Certificate:ISO 9000
Application:Industrial ceramic grinding mediagrinding
Self Abrasion:0.0055-0.01%
Density:3.60g/cm33.7g/cm3
Al2O3 content:92%,95%
Making type:Rolling; ISP
Moh's hardness:9
HRA: 85
Water absorption:0.01%
Type:Ceramic Balls,alumina grinding media balls
Appearance:Smooth and white
Color:white
Compressing strength:2000Mpa
Size:0.5mm-95mm
Advantage: High wear resistance
Production temperature:1600
HS code:690912
Fe2O3:0.02%
Certificate:ISO 9000
Application:Industrial ceramic grinding media
Self Abrasion:0.0055-0.01%
Al2O3 content:92%,95%
Making type:Rolling; ISP
HRA: 85
Type:Ceramic Balls,alumina grinding media balls
Appearance:Smooth and white
Color:white
Compressing strength:2000Mpa
Size:0.5mm-95mm
Advantage: High wear resistance
HS code:690912
Certificate:ISO 9000
Application:Industrial ceramic grinding media
Self Abrasion:0.0055-0.01%
Al2O3 content:92%,95%
Making type:Rolling; ISP
HRA: 85
Type:Ceramic Balls,alumina grinding media balls
Appearance:Smooth and white
Color:white
Compressing strength:2000Mpa
Size:0.5mm-95mm
Advantage: High wear resistance
HS code:690912
Certificate:ISO 9000
Application:Industrial ceramic grinding mediagrinding
Self Abrasion:0.0055-0.01%
Density:3.60g/cm33.7g/cm3
Al2O3 content:92%,95%
Making type:Rolling; ISP
Moh's hardness:9
HRA: 85
Water absorption:0.01%
Type:Ceramic Balls,alumina grinding media balls
Appearance:Smooth and white
Color:white
Compressing strength:2000Mpa
Size:0.5mm-95mm
Advantage: High wear resistance
Production temperature:1600
HS code:690912
Fe2O3:0.02%
Certificate:ISO 9000
Application:Industrial ceramic grinding media
Self Abrasion:0.0055-0.01%
Al2O3 content:92%,95%
Making type:Rolling; ISP
HRA: 85
Type:Ceramic Balls,alumina grinding media balls
Appearance:Smooth and white
Color:white
Compressing strength:2000Mpa
Size:0.5mm-95mm
Advantage: High wear resistance
Production temperature:1600
HS code:690912
Certificate:ISO 9000
Application:Industrial ceramic grinding media
Self Abrasion:0.0055-0.01%
Al2O3 content:92%,95%
Making type:Rolling; ISP
HRA: 85
Type:Ceramic Balls,alumina grinding media balls
Appearance:Smooth and white
Color:white
Compressing strength:2000Mpa
Size:0.5mm-95mm
Advantage: High wear resistance
HS code:690912
Certificate:ISO 9000