2. Columns are 6x6 inches (150x150 mm), use 7 pieces of 3 mm steel bar with stressing system, length is depend of your requirement.
Detail of erection.
Make a foundation for columns of 2x2x2 feet and feel with concrete, then insert sheet in between two columns.
Size and thickness of the panels
3. 7x1 feet and 2 inch thickness
A sketch showing the panels details.
4. Length 7 feet (2100 mm), height 1 feet (300 mm), width 2 inch (50 mm), use 3 mm steel bar with stressing system.
Technical details of the product.
5. Vertical concrete posts as well as horizontal planks is caste using pre-stress technology with designed concrete mix to achieve maximum durability and strength.
Time of delivery
6. 3-4 days after receiving order.
Supplier: Rcc compounds boundary wall, rcc tiles & rcc chairs etc. Services: Transportation & shipping over all india etc. Buyer: Dust , stone , hy carban wire & ms wire etc.
BuildWell Quickbond is a admixture of sand, cement and superior quality polymers. It is a bonding agent
that enables quick preparation of ceiling and RCC wall surface. Also offers the dual benefits of mechanical
and chemical bonding, which eliminates the labor – intensive hacking and reduces debonding losses.
Features :
- Excellent bonding.
- No hacking is required on RCC wall.
- Hence prevention of microcracking and
saving of labor cost.
- Strong chemical and mechanical bond
- Easy to use.
- Works good for Gypsum plaster as well
for cement sand plaster
Benefits :
- Can be easily applied by brush.
- Reduces hacking.
- Time saving.
- Less rebound loss while plastering.
- It is water soluble product hence no
solvent odour.
- Fast drying.
- Improves bonding strength between
RCC wall and Plaster.
* K-SILICATE is used for jointing Acid Resisting brick in construction of vessels in suited for construction of fume chambers and stacks handling hot, dry Acid fumes and vapors.
It is also used for jointing chemical resisting stoneware pipes.
K-SILICATE cement is good bedding material for Acid â?? Resisting bricks and tiles.
The concrete surface needed protection should be dryed, clean and rough.
The bricks or tiles will be set with K-SILICATE cement over concrete surface applied with a suitable an impermeable interliner.
When Bedding and Jointing Materials are the same.
On the treated surface bricks or tiles are bedded to a thickness of about 6 mm and tamp gently with a wooden piece till the paste squeezes out of joints.
The paste that is squeezed out of the joint should be removed by trowel with good finishing. After the mortar of the joint is dryed treat the joints with 20% Hydrochloric Acid Solution by means of brush. A.R.lining should be always in contact with Acid and not with water.
Concrete subtract like Floor, Wall, tanks and similar surface should be protected with a membrane of Bitrok Mastic or compound steel tanks should be protected with rubber or PVC subjected to chemical conditions and temperature of chemical media. The Brick lining is recommended over the protective layer of Bitrok Mastic.
When Bedding and Jointing Materials are Different.
Spread the silicate type mortar about 6 to 8 mm thick on the back of the tile or brick. Press the tile on the bed leaving required space for joints between tiles for bricks. After the bedding mortar is set, fill Mp the joints with specified cement.PRODUCT DATA SHEET FOR SK-HB ( K-SILICATE) MORTAR
A general purpose cement for acid conditions Resistant to High & medium concentrations of most of the common organic and inorganic acids except Hydroflouric acid. Recommended where the concentration of the acid is high suitable for high temperature. Unsuited to aqueous solutions, alkaline conditions.
PREPARATIONS OF MORTAR :
* Measure 1 part by weight of K-SILICATE solution into a suitable mixing pan.
* Add slowly and gradually 3 parts by weight K-SILICATE mortar and mix thoroughly to form a smooth mortar.
* In hot season very large batches of mortar will become stiff quite rapidly therefore small batches, not exceeding 4 to 8 kgs. Will be prepared.
* The cement mortar will be used before it starts setting.