Calcined Anthracite coal is produced when Anthracite is calcined under the temperature of 1240 in vertical shaft furnaces, mainly used in electric steel ovens, water filtering, rust removal in shipbuilding and production of carbon material.
Specification of carbon raiser:
FC: 85% 88% 90% 91% 92% 93% 94% 95%
Sulfur: 0.3%
Ash: 3.5% 4.5% 5.5% 6.5% 8.5% 11.5%
VM: 1.5%
Moisture: 0.5%
Size: 1-3mm, 1-4mm, 1-5mm
1), High purity
- Control the consistency of raw material from the mine resource.
- Introduce automatic whole-process equipment to ensure product consistency.
2), Good performance
- Increase globular graphite amount in the nodular cast iron significantly to promote the graphitization;
- Increase the graphite crystal nucleus of molten iron, refine graphite in the matrix for more uniform distribution;
3), Fine classification
- Various product category, to provide customized carbon raising scheme
4), Cost-saving
- Reduce the usage amount of iron, increase scrap consumption, and save raw material cost.
For 0-5 T furnace use:
While a small amount molten iron in the furnace
Or with some molten iron remained. add the carbon additive one-time
Then add the other material
Which can make carbon additive fully absorbed.
For greater than 5 T furnace
Mix proper carbon additive with charging material as suggested first,
And then along with the increase of furnace charge down into the furnace inside gradually.
That is, before the molten metal rising up to about 2/3 height of furnace
All carbon additive shall be added
It guarantees sufficient melting absorbing time before molten metal out, and improves the absorption of carbon.
Selected Anthracite Coal Granular Activated carbon for amine purify ,remove EDA, MEDA, DIPA, etc
Granular Coal based activated carbon is made from coal though high temperature activation .It is black in appearance, non-toxic and tasteless, with large pores. It is featured by strong adsorption capacity, high wear-resistant performance etc. It is evtensively applied to solvent recovery, catalyst carriers, gas adsorption and water purification in the field of chemicals, environmental protection, power plant, electronics, petrochemical industry, farming, medicine, marine transportation.
Packing
25kg PVC bags+1MT big bag or as customers'requested
Trade terms
FOB CNF CIF
Payments
terms
1).T/T 30%advance ,
2).the balance against copy of B/L
Delivery time
After we receive deposit within 7-10days
Sample
Sample is free within 1kgs
Anthracite Coal is the highest grade of coal, known for its high carbon content, low impurities, and energy efficiency. It burns cleaner and hotter than other types of coal, making it ideal for heating, industrial applications, and producing high-quality coke for steel manufacturing.
Our products can comply with the following requirement :
1 FC 98.5% min
2 S 0.05% max
3 N 0.03% max
4 H 0.03% max
5 Ash 0.5% max
6 Volatile 0.5% max
7 Moisture 1.0% max
8 Partical size :
0-0.2mm 0.2-1.0mm 1.0-4.0mm 1.0-5.0mm 4.0-10mm 5.0-10mm
1 small bag in jumbo bag
2 1mt bag
3 other package
Property In order to make up for the loss of carbon in the smelting process of iron and steel, the carbon containing substances added are called carburants
There are many kinds of additives, and the production process is different. There are wood carbon, coal carbon, coke, graphite and so on. There are many kinds of different kinds. A high - grade carbon - carburizer generally refers to a graphitized carbon - based additive, which in high temperature is graphite in the microform of graphite. The graphite can reduce the content of impurities in the carburizing agent, increase the carbon content of the carbon and reduce the sulfur content.
The use of carburizer in casting can greatly increase the amount of scrap steel, reduce the amount of pig iron, or use no pig iron. The feeding method of furnace smelting should be put into the furnace with waste steel and other materials, and the small dosage can be added to the surface of the molten iron. However, it is important to avoid large quantities of iron and water in order to prevent excessive oxidative effects and insufficient carbon content of casting. The amount of carbon added is determined according to the ratio of other raw materials and carbon content. Different types of cast iron are selected according to the need to choose different types of carbon. The characteristics of the carburizing agent itself choose pure carbon graphitized material, reduce the impurities in pig iron, and the choice of carbon addition agent can reduce the production cost of the casting.