Product Description
"RT-105 is a heavy grade fiberglass reinforced biaxially-oriented polyester film tape with a aggressive solventless pressure sensitive hot melt adhesive. Exhibits
Steady strength excellent adhesion to kraft cartons and bundling applications, etc."
Main Application
* Unitizing
* Strapping
* Packaging
* Transport securing,
* Bundling and palletzing, etc
Construction
*Backing:Polyester film*Adhesive:Pressure sensitive hot melt
*Backing Color:Clear *Reinforcement:Mono-directional continuous glass yarn
Typical Physical Properties
Note: The following technical information and data should be considered representative or typical only, and should not be used for specification purposes.
Typical Physical Properties
Total Thickness:"0.18 mm "ASTM D-3652
Adhesion to Steel: 30 N / inchASTM D-3330
Tensile strength: 1,700 N/cm ASTM D-3759
Elongation at Break:3~5%ASTM D-3759
Service Tem recommended:-7 ~75 ( 20 ~167°F)
Storage Conditions
Store behind present stock. Store in a clean, dry place. Temperature of 4~26 (40~80 ) and 40~50% relative humidity are recommended. Rotate your stock.
Product Description
RT-1C02 is coated by 28um polypropylene film woven with cross fiberglass reinforcements with a pressure-sensitive hot melt adhesive. Balanced machine direction and cross direction tensile strength, high adhesion and medium impact strength. Bi-directional filaments provide resistance to delamination for improved one piece removability and increased boardiness for automatic application.
Main Application
* Unitizing
* Strapping
* Bundling
* Transport securing
* Packaging and palletzing
Construction
*Backing:Polypropylene film*Adhesive:Pressure sensitive hot melt
*Backing Color:Transparent*Reinforcement:2-ways continuous glass yarn
Typical Physical Properties
Note: The following technical information and data should be considered representative or typical only, and should not be used for specification purposes.
Typical Physical Properties
Total Thickness:0.12 ± 0.005mmASTM D-3652
Adhesion to Steel81 oz / inASTM D-3330
Tensile strength:93 lbs./ in(160.5N /cm)ASTM D-3759
Elongation at Break:3ï½?5%ASTM D-3759
Service Tem recommended-7 ~75 ( 20 ~167°F)
Storage Conditions
Store behind present stock. Store in a clean, dry place. Temperature of 4~26 (40~80 ) and 40~50% relative humidity are recommended. Rotate your stock.
Product Description
RT-1C08 is coated by polyester film woven with cross fiberglass reinforcements with a pressure-sensitive hot melt adhesive. Balanced machine direction and cross direction tensile strength, high adhesion and medium impact strength. Bi-directional filaments provide resistance to delamination for improved one piece removability and increased boardiness for automatic application.
Main Application
* Unitizing
* Strapping
* Bundling
* Transport securing
* Packaging and palletzing
Construction
*Backing:Polyester film*Adhesive:Pressure sensitive hot melt
*Backing Color:Transparent*Reinforcement:Cross weaven glass yarn
Typical Physical Properties
Note: The following technical information and data should be considered representative or typical only, and should not be used for specification purposes.
Typical Physical Properties
Total Thickness:0.16 mmASTM D-3652
Adhesion to Steel35 N/25mmASTM D-3330
Tensile strength:800 N/25mmASTM D-3759
Elongation at Break:3ï½?5%ASTM D-3759
Service Tem recommended-7 ~75 ( 20 ~167°F)
Storage Conditions
Store behind present stock. Store in a clean, dry place. Temperature of 4~26 (40~80 ) and 40~50% relative humidity are recommended. Rotate your stock.