Item Test condition Test Method Value Unit
Density ISO 1183 0.944-0.955 g/cm3
MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min
Tensile strength at yield ISO 527-2 22 MPa
Elongation at break ISO 527-2 >350 %
ESCR F50,50 C,100% ASTM D-1693A 1000 h
VICAT ASTM D-1525 126 C
For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.
Item Test condition Test Method Value Unit
Density ISO 1183 0.944-0.955 g/cm3
MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min
Tensile strength at yield ISO 527-2 22 MPa
Elongation at break ISO 527-2 >350 %
ESCR F50,50 C,100% ASTM D-1693A 1000 h
VICAT ASTM D-1525 126 C
HDPE Film A Grade Plastic Scrap For Sales
MATERIAL : HDPE Film A Grade
CATEGORY : HDPE
TYPE : Film
GRADE : A
SPECIFICATION : HDPE has a slight stain on the surface due to the press machine.
ORIGIN : Japan
LOADING WEIGHT : 18-20 Tons
CFR (USD/Ton): 550-750 Vietnam
Item Test condition Test Method Value Unit
Density ISO 1183 0.944-0.955 g/cm3
MFR 190 C/2.16kg ISO 1133 0.03-0.07 g/10min
Tensile strength at yield ISO 527-2 22 MPa
Elongation at break ISO 527-2 >350 %
ESCR F50,50 C,100% ASTM D-1693A 1000 h
VICAT ASTM D-1525 126 C
For extrusion packaging film, rope, woven bags, fishing nets, water pipes; injection of low-end commodity and housing, non-bearing load components, plastic box, turnover box; extrusion blow molding containers, hollow products, bottles.