Tempered and Soaked Glass
Security: It will not hurt people after breaking to pieces,the self-beak rate is lower than 0.1%.
High intensity: It has 4 to 5 times strength than float glass
Hot Stability: It has good hot stability, which can endure 3 times temperature than float
glass, also can endure changing of above 200C.
Thickness: 3-19mm
Max specification:
Flat tempered glass 3000*8000mm;
Bent tempered glass 3000*5000mm R=1500mm.
Packing: Sea worthy wooden cases with interlayer paper.
JHG tempered glass is from 2-25mm , sizes from 100x100mm to 18000x3300mm .
The tempered glass is widely used for fence , furniture ,window, shower door ,curtain wall , floor .
It is processed by controlled thermal or chemical treatments to increase its strength compared with normal glass, about four times stronger than annealed, glass. When broken, tempered glass fractures into small, relatively harmless pieces, it is widen used for window, door, railing, furniture, vehicle.
JHG silk-screen printed glass is one kind of decorative glass made by printing layer of ceramic ink on the surface of glass through the screen mesh for tempering or heat-strengthening process after. As a result silk-screen printed glass is durable, scratch-proof, solar shading and with anti-glare effect.
Silk screen glass is widely usded for architecture ,home application ,furniture , auto window shild.
Ultra clear float glass also called low iron float glass, is produced by less amount of iron in the molten glass formula(usually from 90-110ppm). This type is more transparent than regular glass and it doesn\'t have that greenish tint. The less iron content can increase the light transparency. ultra clear glass is the best choice for architects and designers when need color-matching.
Specification
Sizes: 914*1830/1220*1830/1830*2440/1650*2140/2140*3300/2140*3660/3300*4500/5100/6000mm
JHG float glass base is mainly located in North China, with the function to offer high qualified architecture, automotive, mirror, furniture, home appliance, solar, greenhouse field glass substrate. The exporting capacity is 200containers per month.
Usage: building
Type: tempered
Technique: tempered glass
Trademark: creationclassic
Origin: shandong, china
Shape: curve and flat
Means of transportation: by ship, air, train
Color: clear or tinted
Thickness: 3-19mm
Specification: iso9001, ccc, ce, sgs
Hs code: 70071900
Product description
Heat soaked tempered glass
The heat soak process:
Reach 290â° c â± 10â° c and maintain temperature for 2-8 hrs
Specifications
Max size: 6000mmã?2500mm
Min size: 300mmã?200mm
Thickness: 3mm-19mm
Quality standard: as/nzs2208, gb 15763.4-2009
Heat soaking is a destructive process in which a pane of tempered glass is subjected to temperatures up to 280â° c for several hours over a specific temperature gradient to induce fracture. This test insures that if there is probability of breakage then the infected panes break inside the furnace at the factory itself. Up to 95% panels are usually destroyed inside the heat soak chamber at the factory premises and hence reduce the chances of onsite breakages.
Applications
- window and door
- facades and curtain walls
- automobile, train, vessel
- furniture and decoration
*More than 10 years manufacturer and supplier experience
*Quick delivery of 15 days.
*Australian Standard: AS/NZS 2208:1996safety glazing matererials
*Safety strong packing and loading
*Option processing clear ,frosted ,heat soaked,heat strengthened
*Edging:Flat edge,grind edge,polished edge,beveled edge and others.
Tempered Glass/Toughened Glass
Tempered glass is made by heating float glass to its softening point ( 650700�°C )and then suddenly cooling down to form compression in the surface layer of the glass, thus the mechanical strength is increased by 5 times.
Features:
1.5 times harder than ordinary float glass.
2. Tensile strength for float glass 40 MPa (N/mm2) ,tempered glass , 120200 MPa (N/mm2)
3.Quality standard AS/NZS 2208:1996
4.It withstands abrupt temperature change of 220 Centigrade.
5.Once breakage occurs, the glass disintegrates into small cubical fragments, which are relatively harmless to human body.
Specification:
Flat Tempered Glass
MIN 90x90mm,Max 3660x2140mm
Thickenss 4mm,5mm,6mm,8mm,10mm,12mm,15mm,19mm
Bent/Curved Tempered Glass
Max.Size 2200x750(mm)
Min Size 400*300(mm)
Thickness 519(mm)
Min.benting Radius 370mm
Applications:
1. External use of windows, doors, curtain wall, shopfronts, offices, houses, shops etc.
2. Interior glass screens, partitions, balustrades etc.
3. Shop display windows, showcases, display shelves etc.
4. Furniture, tabletops, picture frames etc.
1. Interlay paper between two sheets
2. Timber end caps
3. Iron/plastic belt for consolidation
4. Safety corner
Density2.5g/cm
Tensile Strength120200 MPa (N/mm2)
Compressive Strength 1000 N/mm 2
Yong's Module73 Gpa
Coefficient of linear expansion 9 x 10 6 m/Mk
softening point 650700�°C
Thickness4mm,5mm,6mm,8mm,10mm,12mm,15mm,19mm
Payment term (1) 30% deposit ,balance paid against the copy of B/L
payment term (2) 30% deposit ,balance will be L/C at sight
Delivery time 15 days after received the deposit
Packing End caps pakcing within stripe and paper
MOQ 1000 Square meter
Loading portQingdao port
Australian Standard: AS/NZS 2208:1996safety glazing matererials
JHG Ultra clear float glass is produced by less amount of iron in the molten glass formula.
This type is more transparent than regular glass and it doesn't have that greenish tint.
The less iron content can increase the light transparency.ultra clear glass is the best choice for architects and designers when need color-matching.
Thickness is from 2-25mm
Jumbo size 3660x18000mm