Ammonium Polyphosphate(App)

Ammonium polyphosphate
For this product, there are 4 specifications i could supply. ( app-0, app-1, app-2, app-3 )

App-0
1) use: flame retardant chemicals, used in paint, coating, rubber & plastic
2) specification:
P2o5: 71.0% min
N : 14.0% min
Polymerization degree: 900 min
Specific gravity: 1.9g/cbm
Temperature of resolving: 270íµ
Solution degree: 0.05g/100ml h2o
Particle diameter: according

App-1
1) use: flame retardant chemicals, used in paint, coating, rubber & plastic
2) specification:
P2o5: 71.0% min
N : 13.5% min
Polymerization degree: 900 min
Specific gravity: 1.9g/cbm
Temperature of resolving: 270íµ
Solution degree: 0.145g/100ml h2o
Particle diameter: according

App-2
1) use: flame retardant chemicals, used in paint, coating, wood
2) specification:
P2o5: 68.0% min
N : 13.0% min
Polymerization degree: 50
Specific gravity: 1.74g/cbm
Temperature of resolving: 270íµ
Solution degree: 2.5g/100ml h2o
Particle diameter: according

App-3
1) use:
-- flame retardant chemicals, used in paper, wood, textile fabric
-- fertilizer chemicals, used in agriculture, etc...
2) specification:
P2o5: 40.0% min
N : 25.0% min
Solution degree: 30g/100ml h2o
Particle diameter: according

25kgs or 500kgs per bag.

It can be used in intumescent fireproof coatings and thermoset resins, such as polyurethane, UP resin and epoxy resin. It can also be used in the retardant of fiber, wood ,rubber and plastic products. Due to its high molecular weight(n>1000) and good heat stability, APP can be used as main ingredient of expanding retardant thermoplastic.,especially used in the PP achieving UL94-V0 for electronic unit.

CAS Number: 68333-79-9
Whiteness:90 Min.
Uses:

Ammonium Polyphosphate II is used as flame retardant insolvent based and water based intumescent coatings. APP II is also used as flame retardant in unsaturated polyesters, epoxies, polyurethanes and flexible and rigid urethane foams.

Appearance-white powder.

P2o5%-72.0 min.

N %-4.0 min.

Density(cm3)-1.9

Decomposition temperature-75.0 min.

Solubility in water(25 100ml h2o) g-0.3 max.

Particle size u-15.0 max.7







PH-.5.0

Usage: intumes

Cent coatings, adhesive, sealants, pu foam.

Appearance-white powder.

P2o5%-72.0 min.

N %-4.0 min.

Density(cm3)-1.9

Decomposition temperature-75.0 min.

Solubility in water(25 100ml h2o) g-0.3 max.

Particle size u-15.0 max.7







PH-.5.0

Usage: intumes

Cent coatings, adhesive, sealants, pu foam.

) 6.5-7.5
Viscosity (10% aqueous suspension, at 25¡ãC) <100
Moisture (w/w) <0.25%
Average Partical size (D50) 10µm


Specification TF-FR201
Appearance White powder
P2O5 (w/w) ¡Ý71%
N Content (w/w) ¡Ý14%
Decomposition Temperature (TGA, onset) >275¡ãC
Solubility (g/100ml water , at 25ºC) <0.5
pH value ( 10% aqueous suspension ) 6.5-7.5
Viscosity (10% aqueous suspension, at 25¡ãC) <100
Moisture (w/w) <0.25%
Average Partical size (D50) 10µm

Ammonium Polyphosphate (phase-I)
(SCI-FR1-APP)
Molecular formula : (NH4PO3)n n>50 CAS No.: 68333-79-9
Model No. : Ammonium Polyphosphate Phase I(SCI-FR1-APP) Standards : HG/T2770-1996

Properties: Ammonium polyphosphate phase I (SCI-FR1-APP) is an excellent, high-efficiency, environment-friendly and nontoxic inorganic flame retardant, used as flameproof additives for expandable fireproof paint & coating and other flame retardant products.

Specification :
Specification Industry standard
HG/T2770-1996 SCI-Guaranteed value
Appearance White powder White powder
P2O5 Content ¡Ý% 68 69
N Content ¡Ý% 13 14-15
Average polymerization degree n ¡Ý 20 80
pH value ( 10% aqueous solution ) 4.5-6.5 7.0¡À0.5
Solubility in water (g/100ml H2O, 25oC) £¼ ---- 1.5
Moisture £¼%(w/w) ---- 0.5
Average particle size(mesh) ---- 200-325

Property :
1. High content of phosphorus, nitrogen, good flame retardant effect.
2. High polymerization degree, low water-solubility and hygroscopicity.
3. pH value is near to neutral, good thermal stability and compatibility.
4. Low toxicity ( LD50>10g/kg ),safe production and use.

Use :
1. used to prepare many kinds of high-efficiency expandable flameproof coating, the flameproof treatment for multistory building, ships, trains, cables, etc.
2. used in the flameproof treatment for woods, plywood,fiberboard,papers,fibers,etc.
3. used as the main flameproof additive for expandable flame retardant used in plastic,resin,rubber, etc.
4. make into powder extinguishing agent to be used in large area outfire for forest, oil field and coal field,etc.

Packing : 25kg woven bag with plastic liner or 875 kg big bag. It must be stored in places well ventilated and dry, and should not be stored in the open air.

Loading capacity:18mt/20'FCL with pallets, 20mt/20'FCL without pallets.



Packing : 25kg woven bag with plastic liner or 875 kg big bag. It must be stored in places well ventilated and dry, and should not be stored in the open air.

1.Technical Index
Project And Class Appearance Chlorine content
(%) Softening point(C) Hot stability index
(%) Heating loss
(%) Screened residual
(20 mesh)
(%)
First Class White or light yellow powder 68-72 95 0.2 1.0 0.02
Qualified Products 90 0.3

2.Application
(1) Flame retardant for macromolecule polymer
(2) Surface treatment agent for knitted and packing materials.


25kg/kraft paper bag, 20 metric ton per 20'container.

1. Technical Index
Brand Chemical composition (%)
AL2O3 not less than Fire Loss not more than Impurity not more than
SiO2 Fe2O3 NA2O
AH-1 64.5 35 0.02 0.02 0.4
AH-2 64.0 35 0.04 0.03 0.5
AH-3 63.5 35 0.08 0.05 0.6

Physical feature: there are mainly 4 sizes of aluminum hydroxide, 325, 2000 and 3000 mesh.

Note :
(1) AL2O3 content is of the difference of 100% minus firing loss and impurity content.
(2) The chemical composition is calculated of the baking at 110¡À5¡ãC for 2 hour.
(3) The impurity content is treated in line with the number rule of GB8170.

2.Application:
Aluminum hydroxide is the most consumable and applicable inorganic additive flame retardant that does not only resist firing, but also prevents from smoke, dropping or toxic gas. So, it is widely used with gradual increase of the usage, at the sectors of hot solidifying and moulding plastic, synthetic rubber, coating and construction materials.


25kg/plastic woven bag, 20 metric ton per 20'container.