Pu Z/p Anti Corrosive Primer

Description

Two-component air-drying polyurethane based primer containing zinc phosphate as anti corrosive pigment.

Recommended Use :-
It is recommended as a primer for MS surface in OEM applications as well as in Process industries like fertilizer plants, Refineries, Petrochemical industries for protection of steel pipelines and structural from corrosion.

Physical Data :-
COLOUR : Red
FINISH : Matt
SOLIDS BY VOLUME : 40 �± 3%
THEORETICAL SPREADING RATE : 13.33 sq.mt / lit at recommended DFT of 30 �µ
FLASH POINT : Base : Above 23�° C Hardener : Above 30�° C
DRYING CHARACTERISTICS (At 30�° C and 65% Relative humidity) : SURFACE DRY : 30 minutes HARD DRY : Overnight FULL CURE : 7 Days
SHELF LIFE : BASE : 6months HARDENER : 6 months
Surface Preparation
Abrasive blasting to Sa 21/2 Swedish Standards is the best method of surface preparation. In case blasting is not possible, then the surface of steel should be manually cleaned with brass wire brush, coarse emery paper, scraper, etc to remove rust, dust, loose old coating, oil, grease, and other foreign contaminants. It is preferable to give a solvent wipe after surface preparation. The surface should be absolutely dry, moisture and oil free before primer application or Phosphated components by 7-tank pretreatment process of surface preparation.

Application Data :-
MIXING RATIO : Base : Hardener (As per our recommendation)
APPLICATION : By Brush / By Conventional Spray
THINNER : Type 290
POT LIFE : 3 hours min at 30�° C
RECOMMENDED DFT : 30-40 �µ.
OVERCOATING INTERVAL : MIN : 8 hours MAX :24 hours (if it exceeds, the surface should be roughened by emery scuffing grade 320)
COMPATIBILITY : Can be top coated with Epoxy, Polyurethane, Chlorinated rubber and Alkyd finish coatings.

Description

Two-component air-drying polyurethane based primer containing zinc phosphate as anti corrosive pigment.

Recommended Use :-
It is recommended as a primer for MS surface in OEM applications as well as in Process industries like fertilizer plants, Refineries, Petrochemical industries for protection of steel pipelines and structural from corrosion.

Physical Data :-
COLOUR :- Yellow
FINISH :- Matt
SOLIDS BY VOLUME :- 40 �± 3%
THEORETICAL SPREADING RATE :- 13.33 sq.mt / lit at recommended DFT of 30 �µ
FLASH POINT :- Base : Above 23�° C Hardener : Above 30�° C
DRYING CHARACTERISTICS (At 30�° C and 65% Relative humidity) :- SURFACE DRY : 30 minutes HARD DRY : Overnight FULL CURE : 7 Days
SHELF LIFE :- BASE : 6months HARDENER : 6 months
Surface Preparation
Abrasive blasting to Sa 21/2 Swedish Standards is the best method of surface preparation. In case blasting is not possible, then the surface of steel should be manually cleaned with brass wire brush, coarse emery paper, scraper, etc to remove rust, dust, loose old coating, oil, grease, and other foreign contaminants. It is preferable to give a solvent wipe after surface preparation. The surface should be absolutely dry, moisture and oil free before primer application or Phosphated components by 7-tank pretreatment process of surface preparation.

Application Data
MIXING RATIO :- Base : Hardener (As per our recommendation)
APPLICATION :- By Brush / By Conventional Spray
THINNER :- Type 290
POT LIFE :- 3 hours min at 30�° C
RECOMMENDED DFT :- 30-40 �µ.
OVERCOATING INTERVAL :- MIN : 8 hours MAX :24 hours (if it exceeds, the surface should be roughened by emery scuffing grade 320)
COMPATIBILITY :- Can be top coated with Epoxy, Polyurethane, Chlorinated rubber and Alkyd finish coatings.
Application Method
Stir the Base part thoroughly. Mix the base and hardener as per our recommended ratio, by volume. Stir the mix gently to attain homogeneity. Add Thinner Type 290 into the mix, if required, depending on application method, and stir gently for few minutes. Allow the mixture to stand still (maturation) for about 10-15 minutes to initiate the reaction. Strain the paint through Nylon filter cloth of 200 mesh size and apply uniformly over the surface. All equipments used for above should be properly clean.

Application :- By Brush / By Conventional Spray / By Airless Spray

Generally no thinner is required for Brush application, however under adverse environmental conditions about 5% of thinner, by volume, can be added. Apply evenly in crossed manner and ensuring the uniform application. Use quality brushes for paint application.

For Conventional Spray application :-
Thinner : Type 290
Addition : 10-15%
Nozzle Orifice : 1.2 -1.4 mm
Nozzle Pressure : 40-70 p.s.i.
For Airless Spray application :-
Thinner : Type 290
Addition : Max 5%
Nozzle Orifice : 0.28- 0.37 mm
Nozzle Pressure : 1400-1800 p.s.i.

PU Scratch Proof Varnish And Paint For Wood Furniture Doors

Thickness: 15- 20mm

Application : Interior, Exterior, Projects

The deep rich black color textured with tiny grey dots are sure to amplify any exterior or interior projects. It will surely add elegance and sophistication to the spaces such as patios, bathroom floors, flooring, staircases, pavements and kitchen tops among others.

This exquisite granite design comes in varying thicknesses ranging from 15 mm to 30 mm and in honed, polished, matte, leather, litchi and 3d finishes. We can combine this subtle yet timeless granite with other shades of granite to create exquisite looking mosaics and tiles as well.

High quality, innovative technology and years of technical expertise enable us to create brilliant granites. It is our guarantee that spaces built with our granite will be visually striking and long-lasting for decades.

PVA primer is the prime foundation coat to seal the wall surface and it helps attaining adhesion to the subsequent coat

PU Primer White Fire Retardant Wood Paint

PU Anti-bacterial Wood Polish And Paint
PU Sealer Anti-bacterial
CATALYST 50% CO15

PW 1201_Penetrating Primer
Ritver Penetrating Primer is an Acrylic copolymer based primer to penetrate into bare surfaces like masonry, plaster, brick work and other bare constructed structures.