102 Epoxy Zinc Chromate Primer

Brighto Epoxy Zinc Chromate Primer

Price :
3.60 Ltr -USD 29.7
18 Ltr- USD 112.4

Description

Two component Epoxy based anti corrosive primer containing red oxide and zinc chromate as corrosion inhibiting pigments

Recommended Use :-
Recommended as a primer on suitably cleaned mild steel surface in various fertilizer units, refineries, chemical and other plants, transportation industries, steel plants, cement plants, power plants, pulp and paper industries, pharmaceutical industries, etc. for application on tank exteriors, structural steel, pipelines, machineries, vessels, etc. The product is recommended as a primer for mild to moderate service conditions. Not to be recommended for immersed water condition

Physical Data
COLOUR : Red
FINISH : Matt
SOLIDS BY VOLUME : 40 + 3%
THEORETICAL SPREADING RATE : 13.33 sq.mt / lt at recommended DFT of 30 FLASH POINT : Base : Above 23C Hardener : Above 23C
DRYING CHARACTERISTICS (At 65% Relative Humidity & at 30C) : SURFACE DRY : 60 - 90 minutes HARD DRY : Overnight FULL CURE : 7 days
SHELF LIFE : BASE : 6 months HARDENER : 6 months
Surface Preparation
Abrasive blasting to Sa 21/2 Swedish Standards is the best method of surface preparation. In case blasting is not possible, then the surface of steel should be cleaned to St-2/St-3 std. The surface should be absolutely dry, moisture and oil free before primer application

Application Data :-
MIXING RATIO : Base : Hardener (As per our recommendations)
APPLICATION : By Brush / By Conventional Spray / By Airless Spray
THINNER : Epoxy Thinner 190
POT LIFE at 30�°C : 4 hours min at 30�°C
RECOMMENDED DFT : 30 40 �µ.
OVERCOATING INTERVAL : MIN : 8 hours MAX : 24 hours
COMPATIBILITY : Can be over coated with Epoxy, PU, Chlorinated Rubber and Synthetic Enamel finish paints.
Application Method
Stir the Base part thoroughly. Mix the base and hardener as per our recommended ratio, by volume. Stir the mix gently to attain homogeneity. Allow the mixture to stand still (maturation) for about 10-15 minutes to initiate the reaction. Add Epoxy Thinner into the mix, if required, depending on application method, and stir gently for few minutes. Strain the Application : By Brush / By Conventional Spray / By Airless Spray Generally no thinner is required for Brush application; however under adverse environmental conditions about 5% of thinner, by volume, can be added. Apply evenly in crossed manner, ensuring the uniform application. Use quality brushes for paint application.

For Conventional Spray application :-
Thinner : Epoxy Thinner 190
Addition : 10-15%
Nozzle Orifice : 1.2 -1.4 mm
Nozzle Pressure : 40-70 p.s.i.
For Airless Spray application :-
Thinner : Epoxy Thinner 190
Addition : Max 5% if required
Nozzle Orifice: 0.37- 0.42mm
Nozzle Pressure : 1400-1800 p.s.i.

Epoxy Primer -guard Primer Is 2 Component Paint System For Interior Walls

Textile Epoxy Primer

Tweed Grey Primer -super Strength For Cement

Synthetic Red Oxide Primer
Ritver Synthetic Red Oxide Primer Commercial is based on Alkyd resin containing anticorrosive pigments. It is used as a primer coat for many applications especially for protecting the metals and other steel structures against corrosion and is quite versatile. It forms a firm base with good adhesion for Ritver Topcoat Enamels and Ritver Quick Drying Enamels.

ARP326
PLASTIC PRIMER
A transparent single component primer that promotes adhesion of subsequent coats of paint on most plastic substrates particularly those used in automotive.

Description

Two component metallic zinc rich epoxy high performance primer.

Recommended Use :-
The zinc pigment in dry film renders excellent protection to steel structure, tanks, bullets, dam gates, pipelines, plant equipments, jetty, etc. in both interior and exterior exposed conditions of fertilizer units, chemical plants, steel plants, cement plants, pulp and paper industries, ports, power plants, petrochemical and pharmaceutical industry, transformer, machines & other heavy duty OEMs. It also provides cathodic protection to steel and gives good resistance to corrosion at local damaged areas. It is useful in heavy-duty protective paint systems. It is recommended not to expose the primed coat alone to chemical and saline atmosphere for a long time.

Physical Data
COLOUR : Grey
FINISH : Matt
SOLIDS BY VOLUME : 50 �± 3%
THEORETICAL SPREADING RATE : 10 sq.mt / ltr at DFT of 50 �µ
FLASH POINT : Base : Above 23�°C Hardener : Above 23�°C
DRYING CHARACTERISTICS (at 30�°C & at 65% Relative Humidity) : HARD DRY : Overnight FULL CURE : 7 days
SHELF LIFE : BASE : 6 months HARDENER : 6 months
Surface Preparation
Abrasive blasting to minimum Sa 2 1/2 Standards is recommended with a profile of 35 - 75 microns. The surface should be absolutely dry and salt free before application. The primer should be applied preferably immediately or within 4 hours of blasting.

Application Data :-
MIXING RATIO : Base : Hardener (As per our recommendations)
APPLICATION : By Brush / By Conventional Spray / By Airless Spray
THINNER : Epoxy Thinner 190
POT LIFE : 4 hours min at 30�°C
RECOMMENDED DFT : 30 50 µ.
OVERCOATING INTERVAL : MIN : 8 hours MAX : Infinite
COMPATIBILITY : Compatible with Epoxy, PU, Chlorinated Rubber intermediate/finish coat.