T-558-N is a solid-type fatty polyamide resin especially designed for HOT-MELT
STRUCTUAL ADHESIVE uses. It has superior processing properties for its ready-to-apply nature
due to the lower molten viscosity. Optimum application temperature of T-558-N is in the
range of 180C~200C.
T-558-N shows excellent adhesion onto various types of plastics,
and steel, as well as onto many other surfaces, giving very tough bonding and sealing strength.
T-558-N may be applied either by hand or manually operated by hand-guns.
An automatic dispensing equipment with a nozzle or a wheel applicator may also be benefited.
The BS - G705 Polyamide Hot Melt Glue Granules are engineered for robust, flexible bonds, these thermoplastic gems are essential in shoemaking and leather goods. From thermofolding to insole binding, trust these granules for professional results.
Chemical Nature: Copolyimide
Physical Specifications:
Softening Point (R&B): 100 - 110 C
Viscosity at 160 C: 3800-4800 mPa.s
Specific Gravity: 0.98 g/cm
Color: Transparent Amber
Mechanical Specifications:
Maximum Load: 10 N/mm
Ultimate Elongation: 15%
Modulus of Elasticity: 250 N/mm
Other Typical Specifications:
Character
Nontoxic, nonirritating, high flash point and fire point not freeze under low temperature, good viscosity and good congluti-nation. It dissolves in the majority of solvents, never dissolve in the water.
Application
Dimer acid and amine will react to produce much different molecular weight polyamide resin. Mainly used to make graver?or flexo?printing ink, epoxy paint, the curing agent and the epoxy cementing material, lubricant .Dimer acid is used to make hot melt adhesive, which is widely used to make thermoplastic product and joint of electric cable in the posts and telecommunications, the communication equipment.
A solid type fatty polyamide resin synthesized by a polycondensation of mainly the dimerized fatty acid and the alkylenepolyamines.
The major applications is in the rotogravure printing inks .
(a). Good solubility into various conventional industrial solvents.
(b). Superior adhesion onto many kind of substrates.
(c). Good wetting( dispersion,)of the pigments and dyestuffs.
(d). Good resistance to water, oil and chemicals..
(e). Fast release of the solvent from the printed film..
(f). Smooth and hard film surface with high gloss.
(g). Smooth and hard film surface with high gloss, which is suitable for over-printings.
The product is called pp, epe hot melt adhesive, suitable for the adhesion of hard sticky materials such as pp and epe. Softening point at about 80anti-temperature about 70 the opening time in 15-20 s.Our products are non-toxic and insipid. High viscosity, fast curing, easy operation, continuous use without carbonization and yellowing resistance, comply with rosh instructions.
Instructions:
1.Recommended gluing method: dispensing
2.Recommended temperature: 130 to 150
3.If there is carbon deposition in a rubber case or hose, may consult equipment manufacturer, or clean with clean mineral oil under 120.
4.The stickiness of the adhesive can be adjusted by temperature.
5.It is prohibited to mix with other brand hot melt adhesive.
6.After adding material to the hot melt tank, the glue tank cover should be closed immediately to prevent foreign contamination.Td-
This series of products can achieve good adhesion effect, environmental tasteless, high strength adhesion, cold resistance, aging resistance, etc. Excellent performance and stable quality can provide the perfect adhesion scheme to various manufacturers. Belongs to green environmental protection paper filter core special glue. Softening point of 80 degrees or so, oil resistance, water resistance, resistance to high and low temperature alternating, weak acid, excellent aseismic performance and good stick relay, fundamentally solve the industry's long plagued a filter degumming problem such as rubber, plastic shrinkage, crack, is currently the most ideal paper filter adhesive. Room temperature curing, the process is simple, easy to use, can be manipulated manually, can also mechanical operation.
The company supplies thelow - temperature hot melt adhesive, and the low temperature not brittle glue, the quality assurance, welcome the consultation to negotiate. The series is not easy to break at low temperature, and it can guarantee the fastness and reliability of adhesion products. The products are blocky, lolliform, granular, white and yellow products, welcome to inquire.
Fast curing speed and near maximum bonding strength. High adhesion strength, durable and excellent uv light. Good temperature resistance, wide temperature range. Adhesion surface does not require strict treatment, easy to use. Excellent resistance to oil, water, acid, kerosene, ethanol, alkali, heterocyclic hydrocarbon, nuclear radiation, etc. Safety and toxicity characteristics: it has a very slight odor, no inhalation danger, and no toxicity after curing. Storage stability is good, the storage period is one year.
Resin hot melt adhesive, softening point of 80 degrees or so, this series of product is suitable for display rack of goods. They have several models, such as a combination of adhesive, white to transparent block hot melt adhesive, guarantee the robustness and stability of adhesive products, viscosity is extremely strong, without extra adhesive, suitable for all kinds of working environment.
Product td-828 hot melt pressure sensitive adhesive, good adhesion, resistance to aging, softening point 85 degrees, can resist high temperature 80 degrees not melting, -20 degrees do not peel away. The operating temperature is recommended at 165-175 degrees. Nowadays, it is widely used in paperboard, shop display rack, packaging materials, carton, cardboard, color box, glazed box of glazed oil carton, and film carton box... Base material coated with glue. The products have been certified by sgs, which is non - toxic.
This product is suitable for bonding and combination of pearl cotton, softening point of 80 degrees or so, and yellowing resistance, will not affect the product quality and color specifications, such as the maximum extent to ensure the stability of the bonding material, not out of shape. For white colloid form. Epe pearl cotton glue composition analysis, curing material, viscosity, non-volatile detection. Epe pearl cotton glue ingredient analysis, curing content, viscosity, nonvolatile matter detection epe glue is a kind of polymer as the main body of one-component adhesive products, the new solution designed to remove epe materials difficult problem of epe special glue.
1.It has the advantages of room temperature curing, convenient operation, high initial adhesion, transparent, yellow and yellow change, fast positioning and non-toxic. 2. Single component, excellent water resistance, heat resistance, cold resistance, aging resistance, acid and alkali resistance, corrosion resistance, oil resistance and albinism. 3. Through the eu rohs standard, the storage of 1 year will not deteriorate, is the current domestic adhesion nylon plastic adhesive field of the first product. Epe materials dedicated plastic glue adhesive is widely used in epe foam packaging material, suitable for epe foam epe foaming, pp, pvc, sponge, foam, wood, polystyrene material such as glue, as well as the pearl cotton, soft material such as eva adhesive effect is obvious.
This series product viscosity is extremely strong, white stick or granular, also has the yellow granular and stick, softening point of 80 degrees or so, short curing time, widely used for automatic packaging, carton packaging and color box packaging and other kinds of packaging requirements, guarantee the stability of adhesive products to the greatest extent, no deformation, ensure the quality of the goods packaging, do not package materil.
The product is based on a number of similar products in china, and a new kind of single-group strong adhesive is introduced according to the user's requirements. It is suitable for the bonding of carton, paper box, automation, color box and other products. Products which use it are firm and smooth without extra adhesive. The product has wide applicability, stable quality and has been well received by users since it was launched. First, the film products need to be treated with adhesive and then apply the adhesive evenly to the surface with a brush or scraper. The coating thickness is between 0.1 and 0.5mm, according to the paper degree. Hold it at a stop, then add pressure, and after 24 hours, it will be bonding.